Float glass

Float glass is a sheet of glass made by floating molten glass on a bed of molten metal, typically tin, although lead and various low melting point alloys were used in the past. This method gives the sheet uniform thickness and very flat surfaces. Modern windows are made from float glass. Most float glass is soda-lime glass, but relatively minor quantities of specialty borosilicate[1] and flat panel display glass are also produced using the float glass process.[2] The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, which pioneered the technique (invented by Sir Alastair Pilkington) in the 1950s.

ManufactureFloat glass uses common glass-making raw materials, typically consisting of sand, soda ash (sodium carbonate), dolomite, limestone, and salt cake (sodium sulfate) etc. Other materials may be used as colourants, refining agents or to adjust the physical and chemical properties of the glass. The raw materials are mixed in a batch mixing process, then fed together with suitable cullet (waste glass), in a controlled ratio, into a furnace where it is heated to approximately 1500 °C. Common flat glass furnaces are 9 m wide, 45 m long, and contain more than 1200 tons of glass. Once molten, the temperature of the glass is stabilised to approximately 1200 °C to ensure a homogeneous specific gravity.

The molten glass is fed into a "tin bath", a bath of molten tin (about 3–4 m wide, 50 m long, 6 cm deep), from a delivery canal and is poured into the tin bath by a ceramic lip known as the spout lip.[5] The amount of glass allowed to pour onto the molten tin is controlled by a gate called a Tweel.

Tin is suitable for the float glass process because it has a high specific gravity, is cohesive, and immiscible into the molten glass. Tin, however, oxidises in a natural atmosphere to form Tin dioxide (SnO2). Known in the production process as dross, the tin dioxide adheres to the glass. To prevent oxidation, the tin bath is provided with a positive pressure protective atmosphere consisting of a mixture of nitrogen and hydrogen.

The glass flows onto the tin surface forming a floating ribbon with perfectly smooth surfaces on both sides and an even thickness. As the glass flows along the tin bath, the temperature is gradually reduced from 1100 °C until the sheet can be lifted from the tin onto rollers at approximately 600 °C. The glass ribbon is pulled off the bath by rollers at a controlled speed. Variation in the flow speed and roller speed enables glass sheets of varying thickness to be formed. Top rollers positioned above the molten tin may be used to control both the thickness and the width of the glass ribbon.



Once off the bath, the glass sheet passes through a lehr kiln for approximately 100 m, where it is further cooled gradually so that it anneals without strain and does not crack from the change in temperature. On exiting the "cold end" of the kiln, the glass is cut by machines.